Initial enamel wear of glazed and polished leucite-based porcelains with different fusing temperatures.

This study used the radiotracer method to measure the initial enamel wear caused by low- and high-fusing porcelains after glazing or polishing. It also tested the correlation between enamel wear and porcelain surface roughness (Ra). Surface morphology was assessed by optical microscopy. Cylindrical specimens of three porcelains (two high-fusing, one low-fusing) were either autoglazed or polished. Flattened enamel specimens were irradiated with neutrons and submitted to the wear assay for 2,500 cycles in distilled water using a 285 g load; the released beta 32P particles were measured for 10 minutes. For all samples, Ra was recorded with a profilometer before and after testing. Enamel wear was not significantly different for porcelain or finishing method but there was a trend of interaction between the two variables (p = 0.08). A positive correlation was found between enamel wear and the initial Ra of porcelain (r = 0.71). The glazed surfaces of high-fusing porcelains were wavy and had a greater Ra, while the polished surfaces had grooves and pores prior to wear testing. The low-fusing porcelain demonstrated lower Ra and a more homogeneous surface. All abraded surfaces had similar morphology after the wear assay.

Influence of core materials in the microleakage of cast crowns / Influência do material constituinte do núcleo na infiltração de coroas fundidas

Os dentes endodonticamente tratados podem ser restaurados com coroas protéticas cimentadas sobre retentores intra-radiculares metálicos fundidos (RIMF) ou sobre preenchimento retido por pinos pré-fabricados. Clinicamente, verifica-se que, ao longo do tempo, ocorre com freqüência desprendimento da coroa, quando cimentada sobre preenchimento de resina composta. Uma das causas poderia ser a infiltração marginal que as coroas sofrem conforme a variação dos materiais que constituem o núcleo. Dessa forma, determinaram-se três condições experimentais: sete dentes com RIMF, sete dentes totalmente preenchidos com resina composta fotopolimerizável (RC) sobre pino pré-fabricado e sete com remanescente dentinário e preenchimento parcial com a mesma resina composta. Os preparos foram padronizados e moldados. As coroas foram fundidas em NiCr. Após a cimentação com cimento de fosfato de zinco, os corpos de prova foram submetidos à ciclagem térmica e à fadiga mecânica. Em seguida, foram imersos em fuccina básica a 0,05% por 8 horas. Após o seccionamento das coroas, três examinadores aferidos avaliaram visualmente, com lupa de aumento, o grau de infiltração, segundo uma escala de valores. Os dados obtidos foram submetidos à análise de intervalos de confiança, sob nível de 90% de confiança. Concluiu-se que os núcleos de metal fundido comportaram-se de forma semelhante aos núcleos parciais (dentina/RC) com infiltração ao nível cervical e os núcleos totalmente em resina apresentaram maior infiltração, chegando a alcançar o terço médio da parede axial.

Estudo "in vitro" da perda de massa dental humana com o uso de agente clareador caseiro à base de peróxido de carbamida a 10 por cento, comparado ao condicionamento com ácido fosfórico a 37 por cento, utilizando o método radiométrico / \"In vitro\" study of dental loss due to 10 percent carbamide peroxide home bleaching compared to 37 percent acid etching, using the radiometric method

Da observaçäo de um ortodontista, Klusmier em 1960, que percebeu que o uso de antisséptico oral à base de peróxido de carbamida clareava os dentes, surgiu o gel clareador caseiro de dentes vitalizados (Haywood, 1991). O primeiro artigo sobre o uso do clareador à base de peróxido de carbamida a 10 por cento, foi publicado em 1989, por Haywood & Heymann. Hoje, existem inúmeros trabalhos realizados sobre este agente, mas praticamente inexistem estudos sobre a perda de massa dental provocada com o uso desse material clareador. da mesma forma, é de amplo conhecimento que o condicionamento ácido é um procedimento corriqueiro na clínica odontológica, acarretando uma desmineralizaçäo das estruturas dentais, mas clinicamente sem danos aos órgäos dentais, quando corretamente utilizado. A proposiçäo desse trabalho, foi verificar a perda quantitativa de massa dental, com o uso do peróxido de carbamida, e comparar com a perda de massa ocasionada com o condicionamento com ácido fosfórico, durante 30 segundos no esmalte e 15 segundos na dentina. Para a avaliaçäo desta perda foi utilizado o método radiométrico, que consiste na medida do ü²P do esmalte e dentina, transferidos para o material aplicado (gel clareador ou gel de ácido fosfórico). Na irradiaçäo com nêutrons do reator nuclear, o üûP da hidroxiapatita do esmalte e dentina, ativa-se por meio de reaçäo (n,y), formando o ü²P. Utilizou-se também a análise por ativaçäo com nêutrons, para determinar a concentraçäo de fósforo nas amostras de esmalte e dentina de cada elemento dental, e, para determinar a quantidade de fósforo que é perdido após as operaçöes de clareamento e condicionamento com ácido...